7SiMn合金鋼的主要特性：27SiMn的性能高于30Mn2，具有較高的強(qiáng)度和耐磨性，淬透性較高，冷變形塑性中等，切削加工性能良好，焊接性能尚可，熱處理時(shí)，鋼的韌性降低較少，水冷時(shí)仍能保持較高的韌性，但有過熱敏感性，白點(diǎn)敏感性及回火脆性傾向，大多在調(diào)質(zhì)后使用，也可在正炎或熱軋供貨狀態(tài)下使用。

化學(xué)成分

C：0.24～0.32 

Si：1.10～1.40 

Mn：1.10～1.40

P：<0.035 （殘留含量）

S：<0.035 （殘留含量）

Cr：≤0.309(殘留含量)

Ni：≤0.30 （殘留含量）

Cu：≤0.30 （殘留含量）

自由鍛件供應(yīng)商哪家好，就找唐山盛通鍛造有限公司。

The main characteristics of 7SiMn alloy steel: 27SiMn performance is higher than 30Mn2, with high strength and wear resistance, high hardenability, medium cold deformation, good cutting performance, good welding performance, heat treatment, steel Less toughness reduction, high toughness when water cooling, but overheat sensitivity, white point sensitivity and temper brittleness tendency, mostly used after quenching and tempering, also in the case of positive or hot rolling supply use.

chemical composition

C: 0.24 to 0.32

Si: 1.10 to 1.40

Mn: 1.10 to 1.40

P: <0.035 (residual content)

S: <0.035 (residual content)

Cr: ≤ 0.309 (residual content)

Ni: ≤ 0.30 (residual content)

Cu: ≤ 0.30 (residual content)